| Specification |
Application Area: Chemical Industry, Petroleum Industry, Pharmaceuticals Industry, Thermal Energy Industry;
Feature: Abrasion Resistance, Corrosion Resistance, High Temperature Resistance;
Grain Size: 0.045mm;
Single Gross: 1.000 Kg Weight;
Compressive: 62MPa Strength;
Flexural Strength: 36MPa;
Chemical: Carbon Composition;
Product Name: Graphite Process Part;
Ash Content: 0.1%;
Selling Units: Single Item;
Single Package: 1X1X1cm Size;
Application: Motor Parts;
Density: 1.85g/cm3;
|
Application Area: Chemical Industry, Petroleum Industry, Pharmaceuticals Industry, Thermal Energy Industry;
Feature: Abrasion Resistance, Corrosion Resistance, High Temperature Resistance;
Type: Flexible Graphite;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
Shape: O-Ring;
Function: O-Ring Mechanical Seals;
Bulk Density: 1.60--2.10g/cm3;
Compressive Strength: 70-160MPa;
Flexural Strength: 25-70MPa;
Thickness: 8-12;
Work Temperature: 200-500℃;
|
Application Area: Chemical Industry, Petroleum Industry, Pharmaceuticals Industry, Thermal Energy Industry;
Feature: Abrasion Resistance, Corrosion Resistance, High Temperature Resistance;
Type: Flexible Graphite;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
Shape: O-Ring;
Function: O-Ring Mechanical Seals;
Bulk Density: 1.60--2.10g/cm3;
Compressive Strength: 70-160MPa;
Flexural Strength: 25-70MPa;
Thickness: 8-12;
Work Temperature: 200-500℃;
|
Application Area: Chemical Industry, Petroleum Industry, Pharmaceuticals Industry, Thermal Energy Industry;
Feature: Abrasion Resistance, Corrosion Resistance, High Temperature Resistance;
Type: Flexible Graphite;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
Shape: O-Ring;
Function: O-Ring Mechanical Seals;
Bulk Density: 1.60--2.10g/cm3;
Compressive Strength: 70-160MPa;
Flexural Strength: 25-70MPa;
Thickness: 8-12;
Work Temperature: 200-500℃;
|
Application Area: Chemical Industry, Petroleum Industry, Pharmaceuticals Industry, Thermal Energy Industry;
Feature: Abrasion Resistance, Corrosion Resistance, High Temperature Resistance;
Type: Flexible Graphite;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
Shape: O-Ring;
Function: O-Ring Mechanical Seals;
Bulk Density: 1.60--2.10g/cm3;
Compressive Strength: 70-160MPa;
Flexural Strength: 25-70MPa;
Thickness: 8-12;
Work Temperature: 200-500℃;
|