| Specification |
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Material: High Purity Graphite;
Advantages: High Temperature Resistance/ Acid Resistance/ Alka;
Application: Metal Melting/Refining Furnace;
Stock: Should Be Stocked in The Dry Situation;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Material: High Purity Graphite;
Advantages: High Temperature Resistance/ Acid Resistance/ Alka;
Application: Metal Melting/Refining Furnace;
Stock: Should Be Stocked in The Dry Situation;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Application Area: Electronic Industry, Metal Smelting and Casting Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance, Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing and Sintering;
Carbon Content: High-Carbon;
Function: High Temperature Resistance;
Customized: Customized;
After-Sales Service: Life Time Technology Support;
Apparent Density: 1.8-1.9 g/cm3;
Shore Hardness: 48-50;
Electrical Strength: 10-9.5 (Omega mm2/M);
Compressive Strength: 37-42MPa;
Flexural Strength: 78-86MPa;
Average Pore Size: 3.2-2.4um;
Efficient of Thermal Expansion: 4.8-4.4(10-6K);
Ash: 0.1 (10-6K);
Type: Graphite Rod;
Composition: Sic;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Material: High Purity Graphite;
Advantages: High Temperature Resistance/ Acid Resistance/ Alka;
Application: Metal Melting/Refining Furnace;
Stock: Should Be Stocked in The Dry Situation;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
|