| Specification |
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|