| Specification |
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Application Area: Electronic Industry, Metal Smelting and Casting Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance, Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing and Sintering;
Carbon Content: High-Carbon;
Apparent Density: 1.80-1.90g/cm3;
Shore Hardness: 48-50;
Electrical Strength: 10-9.5 (Ωmm2/M);
Compressive Strength: 37-42(MPa);
Flexural Strength: 78-86(MPa);
Average Pore Size: 3.2-2.4 (U M);
Coefficient of Thermal Expansion(10-6K): 4.8-4.4;
Ash (10-6K): 0.1;
Type: Graphite Rod;
Composition: Sic;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|